Effect of Rice Husks as Filler in Polymer Matrix Composites
DOI:
https://doi.org/10.15282/jmes.2.2012.5.0016%20Keywords:
Rice husks, unsaturated polyester resin, water absorption, tensile strength.Abstract
In this study, rice husk-filled polyester composites were produced with rice husks (RH) as the filler and unsaturated polyester resin (UPR) as the matrix. Several percentages of filler loadings were used (10, 15, 20 and 25 wt %) in order to gain insights into the effect of filler content on the mechanical properties and water intake of the composites. The tensile strength of the RH-filled UPR composites was found to decrease as the filler loading increased; however, as it reached 25 wt %, the strength showed a moderate increase. The Young’s modulus showed a remarkable increase for 15 wt % of RH but decreased as the RH percentage increased further to 25 wt %. A water absorption test was conducted and the results showed that the composites absorb more water as the percentage weight of RH increased, which is attributed to the ability of the RH filler to absorb water.
References
Adebisi, A. A., Maleque, M. A., & Rahman, M. M. (2011). Metal matrix composite brake rotor: historical development and product life cycle analysis. International Journal of Automotive and Mechanical Engineering, 4, 471-480.
Aramide, F. O., Oladele, I. O., & Folorunso, D. O. (2009). Evaluation of the effect of fiber volume fraction on the mechanical properties of a polymer matrix composites. Leonardo Electronic Journal of Practices and Technologies, 14, 134–141.
Bachtiar, D., Sapuan, S. M., & Hamdan, M. M. (2010). Flexural properties of alkaline treated sugar palm fibre reinforced epoxy composites. International Journal of Automotive and Mechanical Engineering, 1, 79-90.
Bledzki, A. K., & Gassan, J. (1999). Composites reinforced with cellulose based fibres. Progress in Polymer Science, 24, 221–274.
Dhakal, H. N., Zhang, Z. Y., & Richardson, M. O. W. (2007). Effect of water absorption on the mechanical properties of hemp fibre reinforced unsaturated polyester composites. Composites Science and Technology, 67, 1674–1683.
Jeffrey, K. J. T., Tarlochan, F., & Rahman, M. M. (2011). Residual strength of chop strand mats glass fiber/epoxy composite structures: effect of temperature and water absorption. International Journal of Automotive and Mechanical Engineering, 4, 504-519.
Nourbakhsh, A., Ashori, A., Ziaei Tabari, H., & Rezaei, F. (2010). Mechanical and thermochemical properties of wood-flour polypropylene blends. Polymer Bulletin, 65(7), 691–700.
Nourbakhsh, A., Baghlani, F. F., & Ashori, A. (2011). Nano-SiO2 filled rice husk/polypropylene composites: Physico-mechanical properties. Industrial Crops and Products, 33, 183–187.
Rozman, H. D., Yeo, Y. S., Tay, G. S., & Abubakar, A. (2003). The mechanical and physical properties of polyurethane composites based on rice husk and polyethylene glycol. Polymer Testing, 22(3), 6:17–623.
Tabari, H. Z., Nourbakhsh, A., & Ashori, A. (2011). Effects of nanoclay and coupling agent on the mechanical, morphological, and thermal properties of wood flour/polypropylene composites. Polymer Engineering and Science, 51(2), 272–277.
Yang, G. C., Zeng, H. M., Li, J. J., Jian, N. B., & Zhang, W. B. (1996). Relation of modification and tensile properties of sisal fiber. ACTA Science National University Sunyatseni, 35, 53–57.
Yang, H. S., Wolcott, M. P., Kim, H. S., Kim, S., & Kim, H. J. (2007). Effect of different compatibilizing agents on the mechanical properties of lignocellulosic material filled polyethylene bio-composites. Composite Structures, 79(3), 369– 375.
Yao, F., Wu, Q., Lei, Y., & Xu, Y. (2008). Rice straw fiber-reinforced high-density polyethylene composite: effect of fiber type and loading. Industrial Crops and Products, 28(1), 63–72.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2012 The Author(s)
This work is licensed under a Creative Commons Attribution 4.0 International License.