Quantification of Corrosion on Cu Wire Bonding on Ag-Plated Lead Frame in HCl for Automotive Electronic Application

Syafiqah Afiq Rosli; Azman Jalar; Maria Abu Bakar

doi:10.15282/ijame.21.3.2024.11.0894

Authors

Syafiqah Afiq Rosli Institute of Microengineering and Nanoelectronics, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor, Malaysia
Azman Jalar Institute of Microengineering and Nanoelectronics, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor, Malaysia
Maria Abu Bakar Institute of Microengineering and Nanoelectronics, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor, Malaysia

DOI:

https://doi.org/10.15282/ijame.21.3.2024.11.0894

Keywords:

Automotive electronic, Single outline transistor, Cu wire bonding, Selective corrosion, Pitting-like corrosion, Highly corrosive environment

Abstract

Copper (Cu) wire bonding has been widely used in automotive electronics as an interconnection technology. However, Cu wire bonding faces long-term reliability challenges due to corrosion, particularly when exposed to harsh environments. While the corrosion behavior and mechanisms of bulk-sized Cu metal are well studied, the corrosion behavior of submicron-sized Cu wire bonding in miniaturized components remains unclear. This study investigates the corrosion susceptibility of Cu wire with a 1 mil diameter, bonded to an Ag-plated leadframe in a small-outline transistor (SOT-23) package, commonly used in automotive electronics. The Cu wire bonds were subjected to varying concentrations of hydrochloric acid (HCl), specifically 3 M, 5 M, and 7 M, for exposure durations of 6, 12, and 18 hours. The samples were characterized using a field emission scanning electron microscope to observe the microstructure, and ImageJ software was used to quantify the corrosion of the Cu wire bonds. The findings show that the Cu wire bonding is susceptible to corrosion when exposed to high concentrations of HCl. The corrosion of the microstructure became more severe with increasing HCl concentration and exposure time. The affected area of the Cu wire bonding was 21% after 6 hours of exposure to 3 M HCl, increasing to 100% after 18 hours of exposure to 7 M HCl. This study reveals that the corrosion behavior of Cu wire bonding is a combination of selective and pitting-like corrosion, resulting in localized surface degradation rather than uniform corrosion. These findings provide valuable insights into the corrosion behavior of 1 mil Cu wire bonding in SOT-23 packages under highly corrosive environments.

References

M.A. Alim, M.Z. Abdullah, M.S.A. Aziz, and R. Kamarudin, “Die attachment, wire bonding, and encapsulation process in LED packaging: A review,” Sensors and Actuators, A: Physical, vol. 329, p. 112817, 2021.

L. Su, X. Yu, K. Li, and M. Pecht, “Defect inspection of flip chip solder joints based on non-destructive methods: A review,” Microelectron. Reliability, vol. 110, p. 11365, 2020.

J. Gomes, M. Mayer, and B. Lin, “Development of a fast method for optimization of Au ball bond process,” Microelectron. Reliability, vol. 55, no. 3–4, pp. 602–607, 2015.

H. Zhou, Y. Zhang, J. Cao, C. Su, C. Li, A. Chang, et al., “Research progress on bonding wire for microelectronic packaging,” Micromachines, vol. 14, no. 2, p. 432, 2023.

S. Supramaniam, S. Periasamy, M. Nurhisham, M.A. Bakar, and A. Jalar, “Measurement of aluminium remnant thickness on copper wire bonding using 3D laser scanning microscope,” in Proceeding International Symposium Physical and Failure Analysis of Integrated Circuits, IPFA, pp. 1–6, 2023.

A.Z. Azahar, M.A. Bakar, A. Jalar, and F.C. Ani, “Effect of die deflection during au wire bonding process on bonding quality in overhang semiconductor package,” Journal Materials Engineering and Performance, vol. 33, no. 12, pp. 5836-5845, 2024.

Y. Du, Z. Q. Liu, H. Ji, M. Li, and M. Wen, “The mechanism of Pd distribution in the process of FAB formation during Pd-coated Cu wire bonding,” Journal of Materials Science: Materials Electronics, vol. 29, no. 16, pp. 13774–13781, 2018.

S. Nemoto, T. Maeda, M. Miyajima, Y. Akaike, K. Kitagawa. H. Ishii, et al., “Investigation of Mechanism of Corrosion Resistance of Pd Coated Cu Wire Joint by Pseudo Process,” in 2019 International Conference on Electronics Packaging, ICEP 2019, pp. 56–60, 2019.

S. Klengel, R. Klengel, J. Schischka, T. Stephan, M. Petzold, M. Eto, et al., “Influence of copper wire material to corrosion resistant packages and systems for high temperature applications,” in 2019 22nd European Microelectronics and Packaging Conference and Exhibition, EMPC 2019, 2019.

R.T.H. Rongen, A. Mavinkurve, G.M. O’Halloran, N. Owens, Y. Weber, P. Oberndorff, et al., “Package material selection criteria for high temperature automotive applications,” in Proceedings Electronic Components and Technology Conference, pp. 479–485, 2019.

Y.R. Yoo, G. Kim, S.M. Jeon, H.J. Park, W.W. Seo, J.T. Moon, et al., “Influence of HCl concentration on corrosion behavior between Au or Cu bonding wires and the bond pad for semiconductor packaging,” Materials, vol. 16, no. 23, p. 7275, 2023.

S. Supramaniam, M.A. Bakar, A. Atiqah, A. Jalar, and M.Z. Mohd, “Moisture Content and Early Corrosion Detection of Cu Wire Bonding in a Semiconductor Package,” Journal of Failure Analysis and Prevention, vol. 23, no. 6, pp. 2362–2369, 2023.

J. Alptekin, E. Gopalakrishnan, D.K. Kumaravel, K. Antony, H. Langerak, and O. Chyan, “Investigation of CuAl IMCs corrosion in chloride environment and its prevention strategy,” IMAPS Symposium Conference, vol. 2022, no. 1, pp. 217–224, 2023.

P. Lall, Y. Zhang, and S. Jung, “Corrosion kinetics investigation on Cu-Al alloy in sulfate environment under various temperature and pH values,” in Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITHERM), pp. 1–7, 2023.

M.A. Bakar, A. Atiqah, and A. Jalar, “Review on corrosion in electronic packaging trends of collaborative between academia–industry,” Sustainability, vol. 14, no. 23, p. 15730, 2022.

K.A. Hamid, A.H. Badarisman, A. Jalar and M.A. Bakar, “Investigation of integrated factors in the occurrence of copper wire bonding corrosion of semiconductor packages,” Journal of Physics: Conference Series , vol. 2169, no. 1, p. 012016, 2022.

E. Grimm, “The study of copper corrosion mechanisms using electrochemical experimental techniques,” Master Thesis, University of Louisville, 2022.

P. Zhou and K. Ogle, “The corrosion of copper and copper alloys,” in Reference Module in Chemistry, Molecular Sciences and Chemical Engineering, pp. 478–489, 2018.

Y. Wu, K.N. Subramanian, S.C. Barton, and A. Lee, “Electrochemical studies of Pd-doped Cu and Pd-doped Cu-Al intermetallics for understanding corrosion behavior in wire-bonding packages,” Microelectronics Reliability, vol. 78, pp. 355–361, 2017.

C.P. Liu, S.J. Chang, Y.F. Liu, and J. Su, “Corrosion-induced degradation and its mechanism study of Cu–Al interface for Cu-wire bonding under HAST conditions,” Journal of Alloys and Compounds , vol. 825, p. 154046, 2020.

R. Lei, S. Deng, Y. Qiang, D. Xu, G. Du, D. Shao, et al., “Sunflower stalk extract as a novel green inhibitor on aluminium corrosion in HCl solution,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 687, p. 133358, 2024.

H. Jafari, E. Ameri, M.H. Vakili, and A. Berisha, “Novel Silicon-based schiff-base as corrosion inhibitor for anti-corrosion behavior of API 5L Grade B in 1M HCl,” Materials Chemistry and Physics, vol. 311, p. 128499, 2024.

K.D. Alanazi, B.H. Alshammari, T.Y.A. Alanazi, O.A.O. Alshammari, A.M. Ashmawy, M.M. Aljohani, et al., “Thermodynamic, chemical, and electrochemical studies of Aloe ferox Mill extract as a naturally developing copper corrosion inhibitor in HCl solution,” Scientific Reports, vol. 14, no. 1, p. 11944, 2024.

Y.R. Yoo and Y.S. Kim, “Effects of Pd alloying and coating on the galvanic corrosion between Cu wire and bond pads for a semiconductor packaging,” Coatings, vol. 14, no. 5, p. 544, 2024.

K.J. Chen, F.Y. Hung, and C.Y. Chang, “A study of the sulfidation behavior on palladium-coated copper wire with a flash-gold layer (PCA) after wire bonding,” Electronics, vol. 8, no. 7, p. 792, 2019.

T. Saruwatari, T. Takahashi, A. Ono, Y. Asano, T. Iwasaki, M. Ooida, et al., “Reliability improvement of Cu-wire bonded lead frame package for automotive applications,” in Pan Pacific Microelectronics Symposium (Pan Pacific), pp 1-7, 2017.

M. Eto, N. Araki, T. Yamada, R. Klengel, S. Klengel, M. Petzold, et al., “Effects of alloying elements in high reliability copper wire bond material for high temperature applications,” Microelectronic Reliability, vol. 114, p. 113819, 2020.

G.I. Ashok Kumar, A. Lambert, J. Caperton, M. Asokan, W. Yi, and O. Chyan, “Comparative study of chloride and fluoride induced aluminum pad corrosion in wire-bonded device packaging assembly,” Corrosion Materials Degradation, vol. 2, no. 3, pp. 447–460, 2021.

I. Hamidah, A. Solehudin, A. Hamdani, L. Hasanah, K. Khairurrijal, T. Kurniawan, et al., “Corrosion of copper alloys in KOH, NaOH, NaCl, and HCl electrolyte solutions and its impact to the mechanical properties,” Alexandria Engineering Journal., vol. 60, no. 2, pp. 2235–2243, 2021.

T. Kosec, J. Voglar, P. Močnik, and A. Legat, “Effect of the microstructural properties of copper on corrosion performance,” Corrosion Engineering Science Technology, vol. 56, no. 8, pp. 728–735, 2021