Experimental study of the effects of semi-elliptical defects on the API X52 pipeline and its reparation by welding

Zahi MESSAOUD; Madjid MERIEM-BENZIANE

doi:10.15282/jmes.16.4.2022.09.0733

Authors

Z. Messaoud Laboratory of Rheology and Mechanics, Mechanical Engineering Department, Faculty of Technology, Hassiba Benbouali University of Chlef, P. O. Box 151, Esalem City, Chlef, 02000, Algeria. Phone:+213791835640; Fax: +213 27721794
M. Meriem-Benziane Laboratory of Rheology and Mechanics, Mechanical Engineering Department, Faculty of Technology, Hassiba Benbouali University of Chlef, P. O. Box 151, Esalem City, Chlef, 02000, Algeria. Phone:+213791835640; Fax: +213 27721794

DOI:

https://doi.org/10.15282/jmes.16.4.2022.09.0733

Keywords:

API X52 steel, Defect, Pipeline, Repairing, Semi-elliptical, Welding

Abstract

The aim of the project is to study experimentally the influence of the semi-elliptical defect on the steel of grade API 5L X52 pipeline and its reparation by welding operation to keep the safety of hydrocarbons transport network. The tests have been performed on the specimens with/without semi-elliptical defects by using two ratios a/c and a/t, where the defects issue on the piping systems wall is treated by using the welding operation, which focuses on the filling the defected surface as same thickness of the base wall of the pipeline after removing the defects. The decrease of ultimate stress is mainly evident depending on the size of crack, where they compared to the base metal results. The experimental results showed that the reliability of the welding operation is proved especially in the ratio a/c =1, which is similar to that found in automatically welded. It is proved that the ratio a/t = 0.2 curve exhibits similarity to the base metal curve and their elongation conforms to API standard of steel X52 grade. Clearly, corrosion defects cause degradation of mechanical property in the order of 44% to 50% depending on the ratio of 0 < a/c ≤1 and from 20% to 80% according to the second ration of 0 < a/t ≤0.8. The obtained results proved that the enhanced of mechanical properties by welding reaches to ultimate stress is 559 MPa for the ratio a/t = 0.2 and 531 MPa for the ratio a/t = 0.5. Finally, the experimental results provided that the impact of semi-elliptical defect has effects on the safety of piping systems where welding became as one of among solutions to repair the piping systems.

References

API SPEC 5L, “Specification for Line Pipe”, American Petroleum Institute, 2012.

ASME B31G-2009, “Manual for Determining the Remaining Strength of Corroded Pipelines”. A supplement to ASME B31 Code for Pressure Piping, 2009.

Y. Rezaie, S.M.H. Sharifi, G.R. Rashed, “Probabilistic fracture assessment of snake laid pipelines under high pressure/high temperature conditions by engineering critical assessment,” Engineering Fracture Mechanics, vol. 271, pp. 108592, 2022.

Sh. Zangeneh, H.R. Lashgari, H.R. Sharifi, “Fitness-for-service assessment and failure analysis of AISI 304 demineralized-water (DM) pipeline weld crack,” Engineering Failure Analysis, vol. 107, pp. 104210, 2020.

Standards Australia Limited, Pipelines, “Gas and Liquid Petroleum,” Part 1 - Design and Construction, Standards Australia, pp. 328, 2012.

API RP 5L2, “ Recommended Practice for Internal Coating of Line Pipe for Non-Corrosive Gas Transmission Service”, 2002.

M. Wasim, M.B. Djukic, “External corrosion of oil and gas pipelines: A review of failure mechanisms and predictive preventions,” Journal of Natural Gas Science and Engineering, vol. 100, pp. 104467, 2022.

Z. Tang, Z. Wang , Y. Lu, P. Sun, “Cause analysis and preventive measures of pipeline corrosion and leakage accident in alkylation unit,” Engineering Failure Analysis, vol. 128, pp. 105623, 2021.

B.Wei, J. Xu, Q. Fu, Q. Qin, Y. Baia, C. Sun, C. Wanga et. al., “Effect of sulfate-reducing bacteria on corrosion of X80 pipeline steel under disbanded coating in a red soil solution,” Journal of Materials Science & Technology, vol. 87, pp. 1-17, 2021.

Z. Yan, L. Wang, P. Zhang, W. Sun, Z. Yang, B. Liu et al., “Failure analysis of erosion-corrosion of the bend pipe at sewage stripping units,” Engineering Failure Analysis, vol. 129, pp. 105675, 2021.

R. Ashari, A. Eslami, M. Shamanian, S. Asghari, “Effect of weld heat input on corrosion of dissimilar welded pipeline steels under simulated coating disbondment protected by cathodic protection,” Journal of Materials Research and Technology, vol. 9, no. 2, pp. 2136–2145, 2020.

Pipeline Accident Report NTSB/PAR-11/01, “Pacific Gas and Electric Company Natural gas Transmission Pipeline Rupture and Fire,” San Bruno, California, 2011.

Z.F. Chen, W. Wang, H. Yang, S.T. Yan, Z.J Jin, “On the effect of long corrosion defect and axial tension on the burst pressure of subsea pipelines,” Applied Ocean Research, vol. 111, pp. 102637, 2021.

W. Wang, Y. Wang, B. Zhang, W. Shi, C.Q. Li, “Failure prediction of buried pipe network with multiple failure modes and spatial randomness of corrosion,” International Journal of Pressure Vessels and Piping, vol. 191, pp. 104367, 2021.

B.Q. Chen, X. Zhang, C. Guedes Soares, “The effect of general and localized corrosions on the collapse pressure of Subsea pipelines,” Ocean Engineering, vol. 247, pp. 110719, 2022.

B. A. Chouchaoui, R. J. Pick, “Behaviour of longitudinally aligned corrosion pits,” International Journal of Pressure Vessels and Piping, vol. 67, no. 1, pp. 17-35, 1996.

I. Shtoyko, J. Toribio, V. Kharin, M. Hredil, “Prediction of the residual lifetime of gas pipelines considering the effect of soil corrosion and material degradation,” Procedia Structural Integrity, vol. 16, pp. 148–152, 2019.

L.Y. Xu, Y.F. Cheng, “Reliability and failure pressure prediction of various grades of pipeline steel in the presence of corrosion defects and pre-strain,” International Journal of Pressure Vessels and Piping, vol. 89, pp. 75-84, 2012.

H. Wang, Y. Yu, W. Xu, Z. Li, S. Yu. “Time-variant burst strength of pipe with corrosion defects considering mechano-electrochemical interaction.” Thin-Walled Structures, vol. 169, pp. 108479, 2021.

B.G.N. Muthanna, O. Bouledroua, M. Meriem-Benziane, M.R. Setvati, M.B. Djukic, “Assessment of corroded API 5L X52 pipe elbowusing a modified failure assessment diagram,” International Journal of Pressure Vessels and Piping, vol. 190, pp. 104291, 2021.

A.R. Alian, M. Shazly, M.M. Megahed, “3D finite element modeling of in-service sleeve repair welding of gas pipelines”, International Journal of Pressure Vessels and Piping., vol. 146, pp. 216-229, 2016.

Y. Shuai, X. Wang, J. Wang, H.G. Yin, Y.F. Cheng, “Modeling of mechanical behavior of corroded X80 steel pipeline reinforced with type-B repairsleeve,” Thin-Walled Structures, vol. 163, pp. 107708, 2021.

B. Amadeus, S. Dirk, K. Arne, K. Thomas, “Determination of residual stress evolution during repair welding of high-strengthsteel components,” Forces in Mechanics, vol. 6, pp. 100073, 2022.

F.G. Alabtah, E. Mahdi, F.F. Eliyan, “The use of fiber reinforced polymeric composites in pipelines,” Composite Structures, vol. 276, pp. 114595, 2021.

M. Shamsuddoha, A. Manalo, T. Aravinthan, M.M. Islam, L. Djukic, “Failure analysis and design of grouted fiber-composite repair system for corroded steel pipes,” Engineering Failure Analysis, vol. 119, pp. 104979, 2021.

L.P. Djukic, W.S. Sum, K.H. Leong, W. D. Hillier, T.W. Eccleshall, A.Y.L. Leong, “Development of a fibre reinforced polymer composite clamp for metallic pipeline repairs,” Materials and Design, vol. 70, pp. 68-80, 2015.

J.C. Newman, I.S. Raju, “An empirical stress-intensity factor equation for the surface crack,” Engineering Fracture Mechanics, vol. 12, no. 1-2, pp. 185-192, 1981.

I.S. Raju, J.C. Newman, “Stress-intensity factors for a wide range of semi-elliptical surface cracks in finite thickness plates,” Engineering Fracture Mechanics, vol. 11, pp. 817-829, 1979.

X. Wang, S. B. Lambert, “Stress intensity factors and weight functions for longitudinal semi-elliptical surface cracks in thin pipes”, International Journal of Pressure Vessels and Piping, vol. 65, no.1, pp. 75-87, 1996.

C.Q. Li, S.T. Yang, “Stress intensity factors for high aspect ratio semi-elliptical internal surface cracks in pipes,” International Journal of Pressure Vessels and Piping, vol. 96-97, pp. 13-23, 2012.

S. Strobl, P. Supancic, T. Lube, R. Danzer, “Surface crack in tension or in bending - A reassessment of the Newman and Raju formula in respect to fracture toughness measurements in brittle materials,” Journal of the European Ceramic Society, vol. 32, pp. 1491-1501, 2012.

K. Yuan, Y. Jiang, J. Liu, M. Hong, “2D weight functions of stress intensity factors for high aspect ratio semi-elliptical surface cracks in finite thickness plate,” Theoretical and Applied Fracture Mechanics, vol. 110, pp. 102808, 2020.

K.P. Kou, F.M. Burdekin, “Stress intensity factors for a wide range of long-deep semi-elliptical surface cracks, partly through-wall cracks and fully through-wall cracks in tubular members,” Engineering Fracture Mechanics, vol. 73, pp. 1693–1710, 2006.

A. Zareei, S.M. Nabavi, “Calculation of stress intensity factors for circumferential semielliptical cracks with high aspect ratio in pipes,” International Journal of Pressure Vessels and Piping, vol. 146, pp. 32-38, 2016.

W. Wang, W. Yang, C.Q. Lia, S. Yang, “A new method to determine elasto-plastic J-integral for steel pipes with longitudinal semi-elliptical surface cracks,” Engineering Failure Analysis, vol. 118, pp. 104915, 2020.

C.Q. Li, G. Fu , W. Yang, “Stress intensity actors for inclined external surface cracks in pressurised pipes,” Engineering Fracture Mechanics, vol. 165, pp. 72-86, 2016.

Y. Lei, “J-integral and limit load analysis of semi-elliptical surface cracks in plates under bending,” International Journal of Pressure Vessels and Piping, vol. 8, pp. 31-41, 2004.

L. Xu, L. Zhao, H. Jing, Y. Han, “Characterization of the creep interaction effect for twin semi elliptical surface cracks under combined tension and bending loading,” Engineering Fracture Mechanics, vol. 192, pp. 148-162, 2018.

H.E. Coules, “Stress intensity interaction between dissimilar semi-elliptical surface cracks,” International Journal of Pressure Vessels and Piping, vol. 146, pp. 55-64, 2016.

R. B. Stonesifer, F. W, Brust and B. N. Leis, “Mixed-mode stress intensity factors for interacting semi-elliptical surface cracks in a plate,” Engineering Fracture Mechanics, vol. 45, no. 3, pp.357-380, 1993.

A.M. de Souza Sant Anna, I. Napoleão Bastosc, J.M.A. Rebellod, M.P. Cindra Fonseca, “Influence of hydrogenation on residual stresses of pipeline steel welded joints,” Materials Research, vol. 19, no. 5, pp. 1088-1097, 2016.

M. S. Shaari, M. R. M. Akramin, A. K. Ariffin, S. Abdullah, M. Kikuchi, “Fatigue crack growth behaviour of semi-elliptical surface cracks for an API 5L X65 gas pipeline under tension,” IOP Conference Series:Materials Science and Engineering, vol.308, pp. 012041, 2018.

M.S. Shaari, M.R.M. Akramin, A.K. Ariffin, S. Abdullah, M. Kikuchi, “Prediction of fatigue crack growth for semi-elliptical surface cracks using S-version FEM under tension loading,” Journal of Mechanical Engineering and Sciences, vol. 10, no. 3, pp. 2375-2386, 2016.

M. N. M. Husnain, M. R. M. Akramin and Z. L. Chuan, “Surface crack growth prediction under fatigue load using the S-version finite element model (S-FEM), ” IOP Conference Series:Materials Science and Engineering, vol. 469, pp. 012011, 2019.

M. R. M. Akramin, A. K. Ariffin, M. Kikuchi, M. Beer, M. S. Shaari, M. N. M. Husnain, “Surface crack growth prediction under fatigue load using probabilistic S‑version finite element model,” Journal of the Brazilian Society of Mechanical Sciences and Engineering, vol. 40, no. 522, 2018.

W. Xu, S. Jian, “A calculation method for limit load of the gas pipelines with girth weld surface cracks,” Natural Gas

Industry B, vol. 6, no. 5, pp. 481-487, 2019.

S.W. Hong, J.M. Koo, C.S. Seok, J.W. Kim, J.H. Kim, S.K. Hong, “Fatigue life prediction for an API 5L X42 natural gas pipeline,” Engineering Failure Analysis, vol. 56, pp. 396-402, 2015.

D. Saad, G. Dundulis, R. Janulionis, “Calculation of SIFs for semi-elliptical surface cracks in U-shaped bellows expansion joints of Es-Salam research reactor vessel,” Engineering Failure Analysis, vol. 111, pp. 104481, 2020.

J. Cao, W. Ma, G. Pang, K. Wang, J. Ren, H. Nie, W. Dang, T. Yao, “Failure analysis on girth weld cracking of underground tee pipe,” International Journal of Pressure Vessels and Piping, vol. 191, pp. 104371, 2021.

C. Sakonder , L. Xue , M. Paredes, R. Savioli, D.F.B. Sarzosa, “Directional dependence of critical axial strain in X65 pipeline steel subject to combined internal pressure and bending loading,” International Journal of Pressure Vessels and Piping, vol. 196, pp. 104610, 2022.

K. Yuan, J. Liu, “Two-dimensional weight function for the determination of stress intensity factors for semi-elliptical surface cracks in finite-thickness and finite-width plates,” Theoretical and Applied Fracture Mechanics, vol. 121, pp. 103495, 2022.

S. Hertelé, N. O’Dowd, K.V. Minnebruggen, R. Denys, W.D. Waele, “Effects of pipe steel heterogeneity on the tensile strain capacity of a flawed pipeline girth weld,” Engineering Fracture Mechanics, vol. 115, pp. 172–189, 2014.

R.F. Souza, C. Ruggieri, “Fracture assessments of clad pipe girth welds incorporating improved crack driving force solutions,” Engineering Fracture Mechanics, vol. 148, no. 1, pp. 383-405, 2015.

J.A. Ronevich, E.J. Song, Z. Feng, Y. Wang, C. D' Elia, M.R. Hill, “Fatigue crack growth rates in high pressure hydrogen gas for multiple X100 pipeline welds accounting for crack location and residual stress,” Engineering Fracture Mechanics, vol. 228, pp. 106846, 2020.

K.B. Yoon, C.H. Byun, T.S. Nguyen, J.M. Yu, G.M. Jeon, “Cracking of 5Cr steel tee-pipe during start-up operation in heavy oil upgrade refinery,” Engineering Failure Analysis, vol. 81, pp. 204–215, 2017.

K.B. Yoon, J.M. Yu, T.S. Nguyen, “Stress relaxation cracking in 304H stainless steel weld of a chemical reactor serviced at 560ºC,” Engineering Failure Analysis, vol. 56, pp. 288-299, 2015.

API RP 571, “Damage Mechanisms Affecting Fixed Equipment in the Refining Industry,” American Petroleum Institute, Second ed., 2011.

T. Zhang, W. Zhao, T. Li, Y. Zhao, Q. Deng, Y. Wang, W. Jiang, “Comparison of hydrogen embrittlement susceptibility of three cathodic protected ubsea pipeline steels from a point of view of hydrogen permeation,” Corrosion Science, vol. 131, pp. 104-115, 2018.

Y.D. Han, R.Z. Wang, H. Wang, L.Y. Xu, “Hydrogen embrittlement sensitivity of X100 pipeline steel under different pre-strain,” International Journal of Hydrogen Energy, vol. 44, no. 39, pp. 22380-22393, 2019.

J.J. Hoyos, M. Masoumi, V.F. Pereira, A.P. Tschiptschin, M.T.P. Paes, J.A. Avila, “Influence of hydrogen on the microstructure and fracture toughness of friction stir welded plates of API 5L X80 pipeline steel,” International Journal of Hydrogen Energy, vol. 44, no. 41, pp. 23458-23471, 2019.

A.A. Khalili Tabas, B. Beidokhti, A.R. Kiani-Rashid, “Comprehensive study on hydrogen induced cracking of electrical resistance welded API X52pipeline steel,” International Journal of Hydrogen Energy, vol. 46, no. 1, pp. 1012-1022, 2021.

T.T. Nguyen, J. Park, W.S. Kim, S.H. Nahm, U.B. Beak, “Effect of low partial hydrogen in a mixture with methane on the mechanical properties of X70 pipeline steel,” International Journal of Hydrogen Energy, vol. 45, no. 3, pp. 2368-2381, 2020.

T. An, S. Zhang, M. Feng, B. Luo, S. Zheng, L. Chen, L. Zhang, “Synergistic action of hydrogen gas and weld defects on fracture toughness of X80 pipeline steel,” International Journal of Fatigue, vol. 120, pp. 23-32, 2019.

S. Hertelé, A. Cosham, P. Roovers, “Structural integrity of corroded girth welds in vintage steel pipelines,” Engineering Structures, vol. 124, pp. 429-441, 2016.

L. Wang, Y. Tang, T. Ma, J. Zhong, Z. Li, Y. Zhang, H. Xuan, “Stress concentration analysis of butt welds with variable wall thickness of spanning pipelines caused by additional loads International,” International Journal of Pressure Vessels and Piping., vol. 182, pp. 104075, 2020.

H. Moustabchir, J. Arbaoui, Z. Azari, S. Hariri, C.I. Pruncu, “Experimental/numerical investigation of mechanical behavior of internally pressurized cylindrical shells with external longitudinal and circumferential semi-elliptical defects,” Alexandria Engineering Journal, vol. 57, no. 3, pp.1339-1347, 2018.

J. Lukács, G. Nagy, I, Török, J, Égert, B. Pere, “Experimental and numerical investigations of external reinforced damaged pipelines,” Procedia Engineering, vol. 2, no.1, pp. 1191-1200, 2010.

J.M. Duell, J.M. Wilson, M.R. Kessler, “Analysis of a carbon composite overwrap pipeline repair system,” International Journal of Pressure Vessels and Piping, vol. 85, no. 11, pp. 782-788, 2008.

J.M. George, M. Kimiaei, M. Elchalakani, S. Fawzia, “Experimental and numerical investigation of underwater composite repair with fiber reinforced polymers in corroded tubular offshore structural members under concentric and eccentric axial loads,” Engineering Structures, vol. 227, 111402, 2021.

L.P. Djukic , W.S. Sum, K.H. Leong , Wayne D. Hillier, T.W. Eccleshall, A.Y.L. Leong, “Development of a fiber reinforced polymer composite clamp for metallic pipeline repairs,” Materials & Design, vol. 70, pp. 68-80, 2015.

Y.M. Zhang, D.K. Yi, Z.M. Xiao, Z.H. Huang, S.B. Kumar, “Elasticplastic fracture analyses for pipeline girth welds with 3D semi-elliptical surface cracks subjected to large plastic bending,” International Journal of Pressure Vessels and Piping, vol. 105–106, pp. 90-102, 2013.

W. Yang, Q. Zhou, J. Wang, B.C. Khoo, N. Phan-Thien, “Elasticfield prediction for a welding repaired material using a semi-analytical method,” Applied Mathematical Modelling, vol. 99, pp.,566-584, 2021.

S. Longfei, L. Zhiyong, L. Xiaogang, G. Xingpeng, Z. Yinxiao, W. Wu, “Influence of microstructure on stress corrosion cracking of X100 pipeline steel in carbonate/bicarbonate solution,” Journal of Materials Research and Technology, vol. 17, pp.150-165, 2022.

T. Chen, C. Huang, L. Hua, X. Song, “Experimental study on mixed-mode fatigue behavior of center cracked steel plates repaired with CFRP materials,” Thin-Walled Structures, vol. 135, pp. 486-493, 2019.

T. Chen, C. Huang, “Fatigue tests on edge cracked four-point bend steel specimens repaired by CFRP,” Composite Structures, vol. 219, pp. 31-41, 2019.

E. Mahdi, E. Eltai, “Development of cost-effective composite repair system for oil/gas pipelines,” Composite Structures, vol. 202, pp. 802-806, 2018.

K.Sangeetha Raj and K. Nirmalkumar, “Application of FRP wraps in arresting corrosion of steel structures,” International Journal of Engineering Science Invention Research & Development, vol. 1, no. 3, 2014.

H. Lu, X. Wu, H. Ni, M.A. Azimi, X. Yan, Y. Niu, “Stress analysis of urbangas pipeline repaired by insertedhose lining method,” Composites Part B: Engineering, vol. 183, pp. 107657, 2020.

M. Meriem-Benziane, S. A. Abdul-Wahab, H. Zahloul, B. Babaziane, M. Hadj-Meliani, G. Pluvinage, “Finite element analysis of the integrity of an API X65 pipeline with a longitudinal crack repairedwith single- and double-bonded composites,” Composites Part B: Engineering, vol. 77, pp. 431-439, 2015.

A.A. Abd-Elhady, H. El-Din M. Sallam, I.M. Alarifi, R.A. Malik, T.M.A.A. El-Bagory, “Investigation of fatigue crack propagation in steel pipeline repaired by glass fiber reinforced polymer,” Composite Structures, vol. 242, pp. 112189, 2020.

A.A. Abd-Elhady, H. El-Din M. Sallam, M.A. Mubaraki, “Failure analysis of composite repaired pipelines with an inclined crack under static internal pressure,” Structura l Integrity Procedia, vol. 15, pp. 123-130, 2017.

Z. Li, X. Jiang, H. Hopman, L. Zhu, Z. Liu, “External surface cracked offshore steel pipes reinforced with composite repair system subjected to cyclicbending: An experimental investigation,” Theoretical and Applied Fracture Mechanics, vol. 109, pp. 102703, 2020.

ASTM A370, “Standard Test Methods and Definitions for Mechanical Testing of Steel Products,” ASTM International, PA 19428-2959, United States.

Y. Lei, “J-integral and limit loadanalysis of semi-elliptical surface cracks in plates under tension,” International Journal of Pressure Vessels and Piping, vol. 81, pp. 21-30, 2004.

P. Dai, Y. Wang, S. Li, S. Lu, G. Feng, D. Deng, “FEM analysis of residual stress induced by repair welding in SUS304 stainless steel pipe butt-welded joint,” Journal of Manufacturing Processes, vol. 58, pp. 975-983, 2020.

A. Manai, “A framework to assess and repair pre-fatigued welded steel structures by TIG dressing,” Engineering Failure Analysis, vol. 118, pp. 104923, 2020.

A. Blanco, J.M. Hallen, T.S. Nguyen, T.L. Manh, “Influence of crystallographic texture on susceptibility to stress corrosion cracking mechanism of API 5L X52 steel for sour service,” Engineering Failure Analysis, vol. 119, pp. 105002, 2021.

T.A. Netto, U.S. Ferraz, S.F. Estefen, “The effect of corrosion defects on the burst pressure of pipelines,” Journal of Constructional Steel Research, vol. 61, no. 8, pp.1185-1204, 2005.

M.S.G. Chiodo, C. Ruggieri, “Failure assessments of corroded pipelines with axial defects using stress-based criteria: Numerical studies and verification analyses,” International Journal of Pressure Vessels and Piping, vol. 86, no. 2-3, pp. 164-176, 2009.

S.K. Sharma, S. Maheshwari, “A review on welding of high strength oil and gas pipeline steels,” Journal of Natural Gas Science and Engineering, vol. 38, pp. 203-217, 2017.